Metallography of Al5 Mg and Al10 Mg alloys modified with 2% Zn after thermal aging treatment
DOI:
https://doi.org/10.15665/rp.v23i2.3698Palabras clave:
aluminum-magnesium alloys, aging, heat treatments.Resumen
Modern society has the need to obtain materials with better characteristics that help in the use of various applications, so it has always sought new alloys with weight/resistance ratios. In the current work research was carried out on the influence of the addition of a small amount of zinc (2%) on the mechanical properties of two representative aluminum alloys - Magnesium (Al5 Mg and Al10 Mg). The methodology used has several phases, first with a bibliographic study on the principles and fundamentals of heat treatments, subsequently the design of the laundry was carried out by which the specimens are obtained under optimal conditions for the development of this work. Experimental development consists of the selection of the molding medium, model design, fusion and the process of heat treatment of artificial and natural aging of the modified Aluminium-Magnesium alloy, subsequently analysis of the influence of cooling speed, metallographic analysis and grain size. Concluding the coking at high cooling speeds and the poor colability of the alloy results in a very rapid solidification of the specimen, having the characteristic of a fine grain size and absence of macroscopic porosities, as well as a clean and bright surface finish; the temperature and time of heat treatment had a great influence on the variation in grain size due to the solute concentration of each specimen.
Citas
B. Davó and J. J. Damborenea, "Corrosion and inhibition in medium-strength aluminum alloys," Rev. Metal. Vol 40, No 6, vol. 40, no. 6, pp. 442-446, 2004, doi: 10.3989/revmetalm.2004.v40.i6.304.
R. Falla, K. Quintana, F. Franco, and N. Sanchez, "Mechanical properties of friction stir spot welding in AA6063-T5 aluminum alloy," Rev. Prospect., vol. 10, no. 1, pp. 79-84, 2012, doi: 10.15665/rp.v10i1.399.
J. C. Pereira, L. Durán, D. Deventer, and J. Zambrano, "Torsional mechanical behavior of heat-treated AA6061 aluminum alloy," Suppl. the Rev. Latinoam. Metal. y Mater. vol. 28, no. 2, pp. 183-190, 2009.
A. Cotes-Toro, D. Manco-jaraba, and E. Rojas-Martínez, "Evaluation of mechanical and metallurgical properties of Al 5 Mg and Al 10 Mg alloys modified with 2 % Zn after thermal aging treatment," Prospectiva, vol. 21, no. 1, pp. 23-31, 2023, doi: 10.15665/rp.v21i1.2948.
Á. Cotes-Toro, D. Manco-Jaraba, and C. Robles-Julio, Response to thermal aging heat treatment of Al5Mg and Al10Mg alloys modified with 2 % zinc. Riohacha, Colombia, 2019.
C. Vargel, The behavior of aluminum and its alloys, 7th ed. in Encyclopedia of Aluminum. 1981. [Online]. Available: https://books.google.com.co/books?id=nxiktwEACAAJ
K. Van Horn, Aluminum. Properties, physical metallurgy and phase diagrams. 1967.
F. De Los Reyes and E. Franco, "Characterization of 12Cr1MoV steel aging from imaging techniques," Tecnol. Chem, vol. 29, no. 3, pp. 43-47, 2009.
R. Rodriguez and I. Gutiérrez, "Study of the contribution of phases to mechanical properties in steels with mixed structures," in VIII Congreso Nacional de Propiedades Mecánicas de Sólidos, 2002, pp. 87-96.
D. Reigoza, "Microstructural study by optical microscopy with color metallography techniques on an AKT XM 200 motorcycle piston," Universidad Distrital Francisco José de Caldas, 2017.
I. Polmear, D. StJohn, J.-F. Nie, and M. Qian, Light alloys: metallurgy of the light metals, 5th ed. Butterworth-Heinemann, 2017.
C. J. Aparicio Bádenas, J. M. Manero Planella, D. Rodríguez Rius, A. Andres Doménech, P. M. Arandés, and J. A. Planell Estany, Aleaciones ligeras, 1st ed. Barcelona: Edicions Universitat Politècnica de Catalunya, 2001.
R. M. Nunes et al., Heat Treating, 4th ed. 1991.
R. Nunes et al., ASM Handbook: Properties and Selection: Non Ferreous Alloys and Special-Purporse Materials, Volume 2. 1990.
ASM Handbook Committee, Metallography and Microstructures, 9th ed, vol. 9. USA: Metals Handbook, 1985.
J. E. Hatch, Aluminum: Properties and Physical Metallurgy. in Aluminum / J.E. Hatch Hrsg. American Society for Metals. American Society for Metals, 1984. [Online]. Available: https://books.google.com.co/books?id=dUgzGsEMhoUC
L. Mondolfo, Aluminum Alloys Structure and Properties, 1st ed. 1976. doi: https://doi.org/10.1016/C2013-0-04239-9.
Foseco, "Aluminiun silicon alloys." England.
ASTM Standard E3-11, "Metallographic Sample Preparation." ASTM International, pp. 1-7, 2007.
ASTM Standard E - 407, "Standard practice for micro-etching of metals and alloys." ASTM International, 2015. doi: 10.1520 / E0407-07R15E01.
F. Millán-Delgado, "Fabrication and characterization of recycled aluminum alloy with addition of particulate silicon," Universidad Nacional de Colombia, 2016.
G. Dieter, Mechanical Metallurgy. McGraw-hill New York, 1961.
Publicado
Número
Sección
Licencia
Derechos de autor 2025 Álvaro José Cotes Toro, DINO CARMELO MANCO JARABA, Carlos Alberto Socarras Bertiz
Esta obra está bajo una licencia internacional Creative Commons Atribución-NoComercial-SinDerivadas 4.0.
Los autores/as que publiquen en esta revista aceptan las siguientes condiciones:
- Los autores/as ceden los derechos de autor y dan a la revista el derecho de la primera publicación, con el trabajo registrado con la licencia de atribución de Creative Commons, que permite a terceros utilizar lo publicado siempre que mencionen la autoría del trabajo y a la primera publicación en esta revista.
- Los autores/as pueden realizar otros acuerdos contractuales independientes y adicionales para la distribución no exclusiva de la versión del artículo publicado en esta revista (p. ej., incluirlo en un repositorio institucional o publicarlo en un libro) siempre que indiquen claramente que el trabajo se publicó por primera vez en esta revista.
- Se permite y recomienda a los autores/as a publicar su trabajo en Internet (por ejemplo en páginas institucionales o personales) antes y durante el proceso de revisión y publicación, ya que puede conducir a intercambios productivos y a una mayor y más rápida difusión del trabajo publicado (vea The Effect of Open Access).
Instrucciones para el llenado de la Certificación de Originalidad y la Cesión de Derechos de Autor.
- Haga click aquí y baje el formulario de Certificación de Originalidad y la Cesión de Derechos de Autor.
- En cada uno de los campos para rellenar haga click y complete lo correspondiente.
- Una vez llenos los campos, copie al final su firma escaneada o firma digital. Favor ajustar el tamaño de la firma en el formulario.
- Finalmente, lo puede guardar como pdf y enviarlo a través de la palataforma OJS, como archivo complementario.
Si tiene dudas contáctenos, por favor.