La Resistencia al Desgaste Para Recubrimientos De Carburo de Tungsteno Depositados sobre Sustratos De Acero Rápido por Medio de Rociado Térmico

Authors

  • José Ricardo Sandoval García Pedagogical and Technological University of Colombia image/svg+xml
  • Carlos Mauricio Moreno Téllez
  • Sandra Marcela Acuña Rodríguez

DOI:

https://doi.org/10.15665/rp.v20i1.2841

Keywords:

High-speed steel, Thermal spraying, Tungsten carbide, Wear resistance

Abstract

Abstract.

 

 

For this research, the tungsten carbide coatings were deposited by the thermal spraying technique with an oxyacetylene flame on high-speed steel substrates, in order to improve wear resistance. For the deposit, a high-speed steel was used as a substrate and as a coating commercial tungsten carbide powders reference Eutalloy 10112, which were characterized to identify: composition, microstructure, properties and thermal behavior. The coating was deposited with a CastoDyn DS 8000 equipment, oxidizing flame and projection distance of 140 mm, to analyze aspects such as morphology, thickness and porosity by scanning electron microscopy, adhesion with a pull off test, composition with an X-ray diffraction and hardness with a Vickers-type indenter micro-durometer. To evaluate the resistance of the coating, tribological tests were carried out by pin on disk equipment, the parameters implemented in the test were: 15 and 20 N for travel distances of 500 and 300 m.

References

. S. Kalpakjian, S., S. R Schmid, Manufactura, ingeniería y tecnología. Mexico, Pearson Educación, 2008, pp 613-721.

. D. E. Castillo Gutiérrez, “Caracterización microestructural y mecánica de aceros de fase dual (ferrita-martensita), obtenidos mediante procesos térmicos y termomecánicos”, Ingeniare. Revista chilena de ingeniería, 26 (3), 430-339,2018.

. M. P Groover, Fundamentals of modern manufacturing. Estados Unidos, JOHN WILEY & SONS, INC.2007, pp 507-600

. Y. Qiu, “Improvement of tribological performance of CrN coating via mltilayering with VN”, Surface & Coatings Technology, 231, 357–363,2013

. V. Chayeuski, “Characteristics of ZrC/Ni-UDD coatings for a tungsten carbide cutting tool”, Applied Surface Science, 446, 18–26,2018.

. T. S. Kumar, “Comparative evaluation of performances of TiAlN, AlCrN, TiAlN/AlCrN coated carbide cutting tools and uncoated carbide cutting tools on turning Inconel 825 alloy using Grey Relational Analysis”, Sensors and Actuators A: Physical, 279, 331–342.2018.

. J. A. Morales Torres, J. J. Olaya Flórez, “Una aproximación a la tecnología de proyección térmica”, Avances Investigación en Ingeniería, 9 (2), 60-71,2012.

. R. J Wood, S Herd, M. R Thakare, “A critical review of the tribocorrosion of cemented and thermal sprayed tungsten carbide”, Tribology International, 119, 491-509.2018.

. Castolin Eutectic, “Manual CastoDyn DS 8000”, manual de funcionamiento, España,Castolin España, pp 1-37.

. J. A. Schey, Procesos de manufactura. México, Mcgraw-hill/interamericana editores, 2002, pp. 637-750.

. ASM Vol 16, Metals Handbook. Machining. Ohio, Metals Park, 1990, pp. 100-150.

. Castolin Eutectic, “Eutalloy Thermal Spray Alloys”, Milwaukee,Eutectic Corporation, pp. 1-8.

. ASTM D4541, Standard Test Method for Pull-Off Strength of Coatings Using Portable Adhesion Testers.United States. West Conshohocken,pp.1-13.

. ASTM G99, Standard Test Method for Wear Testing with a Pin-on-Disk Apparatus1. United States. West Conshohocken,pp.1-6.

. J. Archard, “Contact and Rubbing of Flat Surface”. Journal of Applied Physics,(No 24), 982.1953.

. D. M. Coureaux, “Influencia de la microestructura en el comportamiento tribológico de carburos cementados (WC-Co) borados”, Ingeniare. Revista chilena de ingeniería, 23 (2), 259-268.2015.

Downloads

Published

2025-12-16

Issue

Vol. 20 No. 1 (2022): Enero - Junio

Section

Articles

Categories

License

Copyright (c) 2022 José Ricardo Sandoval García, Carlos Mauricio Moreno Téllez, Sandra Marcela Acuña Rodríguez

Creative Commons License

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

The authors to publish in this journal agree to the following conditions:

  1. The authors transfer the copyright and give the the journal first publication right of the work registered with Creative Commons Attribution License, which allows third parties to use the published work on the condition of always mentioning the authorship and first publication in this journal.
  2. The authors may perform other independent and additional contractual arrangements for the non-exclusive distribution of the version of the article published in this issue (E.g., Inclusion in an institutional repository or publication in a book), it must be indicated clearly that the work was first published in this journal.
  3. It allows and encourages the authors to publish their work online (eg institutional or personal pages) before and during the review and publication process. It can lead to productive exchanges and greater and faster dissemination of the published work (see The Effect of Open Access)

Instructions to fill out Certificate of Originality and Copyright Assignment

  1. Click here and get the forms of Certificate of Originality and Copyright Assignment  .
  2. In each field to fill out, click and complete the corresponding information.
  1. Once the fields are filled out, at the end of the form copy your scanned signature or digital signature. Please adjust the size of the signature on the form.
  2. Finally, you can save them as pdf files and send them through the OJS platform as an attachment.

 

How to Cite

La Resistencia al Desgaste Para Recubrimientos De Carburo de Tungsteno Depositados sobre Sustratos De Acero Rápido por Medio de Rociado Térmico. (2025). Journal Prospectiva, 20(1). https://doi.org/10.15665/rp.v20i1.2841